ART. IV.-ON THE MODE OF TESTING BUILDING MATERIALS,

AND AN ACCOUNT OF THE MARBLE USED IN THE EXTEN-
SION OF THE UNITED STATES CAPITOL. By PROFESSOR JOSEPH
HENRY, Secretary of the Smithonian Institution.*

A COMMISSION was appointed by the President of the United States, in November, 1851, to examine the marbles which were offered for the extension of thė United States Capitol, which consisted of General Totten, A. J. Downing, the Commissioner of Patents, the architect, and myself. Another commission was subsequently appointed, in the early part of the year 1854, to repeat and extend some of the experiments,—the members of which were General Totten, Professor Bache, and myself.

A part of the results of the first commission were given in a report to the Secretary of the Interior, and a detailed account of the whole of the investigations of these committees will ultimately be given in full in a report to Congress, and I propose here merely to present some of the facts of general interest, or which may be of importance to those engaged in similar researches.

Although the art of building has been practised from the earliest times, and constant demands have been made, in every age, for the means of determining the best materials, yet the process of ascertaining the strength and durability of stone appears to bave received but little definite scientific attention, and the commission, who have never before made this subject a special object of study, have been surprised with unforeseen difficulties at

Blackwell in his Lecture on the iron-making resources of the United Kingdom, delivered before the Society of Arts in 1852, in speaking of the state of the manufacture in this country, has the following remarkable statement.-“We cannot boast of any exclusive skill in manufacture. In the United States there are now furnaces smelting iron with anthracite coal, and making a weekly produce double or treble that produced by the anthracite furnaces of South Wales."

We are at a loss to conceive Mr. Blackwell's reasons for thus boldly asserting that the British manufacturer was inferior in skin to the American. The average weekly produce of the South Wales anthracite furnace is between 80 and 90 tons; higher makes of 110 to 120 are quite common.

From our extensive acquaintance with American works, we can state, that, the capacity of furnace and quality of ores being alike, the produce of the South Wales furnaces is in excess of the American.

We must direct attention to a circumstance of considerable importance in all estimates of produce and quantities. The estimates of the American makes are generally based on the legal ton of 2,240 lbs., but on other occa

sions their ton is so low as 2,000 lbs. Now the British manufacturer sells at • the legal ton of 2,240 lbs.; but in all estimates of production, payments to

workmen, &c., the ton of iron is 2,400 lbs.; while that of the coal and ore varies from 2,520 to 2,760 lbs.

* From the Proceedings of the American Association for the advancement of Science, held at Providence, R. I., August, 1855. New York: 1856.

every step of their progress, and have come to the conclusion that the processes usually employed for solving these questions are still in a very unsatisfactory state.

It should be recollected, that the stone in the building is to be exposed for centuries, and that the conclusions desired are to be drawn from results produced in the course of a few weeks. Besides this, in the present state of science, we do not know all the actions to which the materials are subjected in nature, nor can we fully estimate the amount of those which are known.

The solvent power of water, which even attacks glass, must in time produce an appreciable effect on the most solid material, particularly where it contains, as the water of the atmosphere always does, carbonic acid in solution. The attrition of siliceous dusts, when blown against a building, or washed down its sides by rain, is evidently operative in wearing away the surface, though the evanescent portion removed at each time may not be indicated by the nicest balance. An examination of the basin which formerly received the water from the fountain at the western entrance of the Capitol, now deposited in the Patent Office, will convince any one of the great amount of action produced principally by water charged with carbonic acid. Again, every flash of lightning not only generates nitric acid, -—which, in solution in the rain, acts on the marble, but also by its inductive effects at a distance produces chemical changes along the moist wall, which are at the present time beyond our means of estimating. Also the constant variations of temperature from day to day, and even from hour to hour, give rise to molecular motions which must affect the durability of the material of a building. Recent observations on the pendulum have shown that the Bunker Hill Monument is scarcely for a moment in a state of rest, but is constantly warping and bending under the influence of the varying temperature of its different sides.

Moreover, as soon as the polished surface of a building is made rough from any of the causes aforementioned, the seeds of minute lichens and mosses, which are constantly floating in the atmosphere, make it a place of repose, and by the growth and decay of the microscopic plants which spring from these, discoloration is produced, and disintegration is assisted.

But perhaps the greatest source of the wearing away in a climate like ours, is that of the alternations of freezing and thawing which take place during the winter season; and though this effect must be comparatively powerful, yet, in a good marble, it requires the accumulated effect of a number of years in order definitely to estimate its amount. From all these causes, the commission are convinced that the only entirely reliable means of ascertaining the comparative capability of marble to resist the weather, is to study the actual effects of the atmosphere upon it, as exhibited in buildings which for years have been exposed to

these influences. Unfortunately, however, in this country, but few opportunities for applying this test are to be found. It is true some analogous information may be derived from the examination of the exposed surfaces of marble in their out-crops at the quarry; but in this case the length of time they have been exposed, and the changes of action to which they may have been subjected, during, perhaps, long geological periods, are unknown; and since different quarries may not have been exposed to the same action, they do not always afford definite data for reliable comparative estimates of durability, except where different specimens occur in the same quarry.

As we have said before, the art of testing the quality of stone for building purposes is at present in a very imperfect state; the object is to imitate the operations of nature, and at the same time to hasten the effect by increasing the energy of the action, and, after all, the result may be deemed but as approximative, or, to a considerable degree, merely probable.

About twenty years ago an ingenious process was devised by M. Brard, which consists in saturating the stone to be tested with a solution of the sulphate of soda. In drying, this salt crystal lizes and expands, thus producing an exfoliation of surface which is supposed to imitate the effect of frost. Though this process has been much relied on, and generally employed, recent investigations made by Dr. Owen, lead us to doubt its perfect analogy with that of the operations of nature. He found that the results produced by the actual exposure to freezing and thawing in the air, during a portion of the winter, in the case of the more porous stones, produced very different results from those obtained by the drying of the salt. It appears from his experiments, that the action of the latter is chemical as well as mechanical.

The commission, in consideration of this, have attempted to produce results on the stone by freezing and thawing by means of artificial cold and heat. This process is, however, laborious; each specimen must be enclosed in a separate box fitted with a cover, and the amount of exfoliation preduced is so slight, that in good marble the operation requires to be repeated many times before reliable comparative results can be obtained. In prosecuting this part of the inquiries, unforeseen difficulties have occurred in ascertaining precisely the amount of the disintegration, and it has been found that the results are liable to be vitiated by circumstances which were not in view at the commencement of the inquiries.

It would seem at first sight, and the commission when they undertook the investigation were of the same opinion, that but little difficulty would be found in ascertaining the strength of the various specimens of marbles. In this, however, they were in error. The first difficulty which occurred was to procure the proper instrument for the purpose. On examining the account

VOL. VII.-4

of that used by Rennie, and described in the Transactions of the Royal Society of London, the commission found that its construction involved too much friction to allow of definite comparative results. Friction itself has to be overcome, as well as the resistance to compression, and since it increases in proportion to the pressure, the stronger stones would appear relatively to withstand too great a compressing force.

T'he commission first examined an instrument-a hydraulic press—which had previously been used for experiments of this kind, but found that it was liable to the same objection as that of the machine of Rennie. They were, however, extremely for tunate subsequently in obtaining, through the politeness of Commodore Ballard, commandant of the Navy Yard, the use of an admirable instrument devised by Major Wade, late of the United States Army, and constructed under his direction, for the purpose of testing the strength of gun metals. This instrument consists of a compound lever, the several fulcra of which are knife-edges, opposed to hardened steel surfaces. The commission verified the delicacy and accuracy of the indications of this instrument by actual weighing, and found, in accordance with the description of Major Wade, the equilibrium was produced by one pound in opposition to two hundred. In the use of this instrument the commission were much indebted to the experience and scientific knowledge of Lieutenant Dahlgreen, of the Navy Yard, and to the liberality with which all the appliances of that impor. tant public establishment were put at their disposal.

Specimens of the different samples of marble were prepared in the form of cubes of one inch and a half in dimension, and consequently exhibiting a base of two and a quarter square inches. These were dressed by ordinary workmen with the use of a square, and the opposite sides made as nearly parallel as possible by grinding by hand on a flat surface. They were then placed between two thick steel plates, and in order to insure an equality of pressure, independent of any want of perfect parallelism and flatness on the two opposite surfaces, a thin plate of lead was interposed above and below between the stone and the plates of steel. This was in accordance with a plan adopted by Rennie, and that which appears to have been used by most, if not all, of the subsequent experimenters in researches of this kind. Some doubt, however, was expressed as to the action of interposed lead, which induced a series of experiments to settle this question, when the remarkable fact was discovered, that the yielding and approximate equable pressure of the lead caused the stone to give away at about half the pressure it would sustain without such an interposition. For example, one of the cubes, precisely similar to another which withstood a pressure of upwards of 60,000 pounds when placed in immediate contact with the steel plates, gave way at about 30,000 with lead interposed.

This remarkable fact was verified in a series of experiments, embracing samples of nearly all the marbles under trial, and in no case did a single exception occur to vary the result.

The explanation of this remarkable phenomenon, now that it is known, is not difficult. The stone tends to give way by bulg. ing out in the centre of each of its four perpendicular faces, and to form two pyramidal figures, with their apices opposed to each other at the centre of the cube, and their bases against the steel plates. In the case where rigid equable pressure is employed, as in that of the thick steel plate, all parts must give way together. But in that of a yielding equable pressure, as in the case of interposed lead, the stone first gives way along the lines of least resistance, and the remaining pressure must be sustained by the central portions around the vertical axis of the cube.

After this important fact was clearly determined, lead and all other interposed substances were discarded, and a method devised by which the upper and lower surfaces of the cube could be ground into perfect parallelism. This consists in the use of a rectangular iron frame, into which a row of six of the specimens could be fastened by a screw at the end. The upper and lower surfaces of this iron frame were wrought into perfect parallelism by the operation of a planing machine. The stones being fastened into this, with a small portion of the upper and lower parts projecting, the whole were ground down to a flat surface, until the iron and the face of the cubes were thus brought into a continuous plane. The frame was then turned over, and the opposite surfaces ground in like manner. Care was of course taken that the surfaces thus reduced to perfect parallelism, in order to receive the action of the machine, were parallel to the natural beds of the stone.

All the specimens tested were subjected to this process, and in their exposure to pressure were found to give concordant results. The crushing force exhibited in the subjoined table is much greater than that heretofore given for the same material.

The commission have also determined the specific gravities of the different samples submitted to their examination, and also the quantity of water which each absorbs.

They consider these determinations, and particularly that of the resistance to crushing, tests of much importance, as indicating the cohesive force of the particles of the stone, and its capacity to resist most of the influences before mentioned.

The amount of water absorbed may be regarded as a measure of the antagonistic force to cohesion, which tends, in the expansion of freezing, to disintegrate the surface. In considering, however, the indication of this test, care must be taken to make the comparison between marbles of nearly the same texture, because a coarsely crystallized stone may apparently absorb a small quantity of water, wbile in reality the cement which unites the